Brand: CEMEDINE
Model: Y600
Product Name: Second Generation Acrylic adhesive | Reactive Acrylic Adhesive
Specifications:
Multi-purpose type
| Y600 | Y600H | Y610 | Y620 |
---|
Agent A | Agent B | Agent A | Agent B | Agent A | Agent B | Agent A | Agent B |
---|
Application / Properties / Features | High speed curing | High viscosity | High strength | Slow curing |
---|
Base | Acrylic resin | Acrylic resin | Acrylic resin | Acrylic resin |
---|
External appearance | Light blue | Blue | White | Gray | White | Gray | Light yellow | Blue |
---|
Viscosity | mPa・s/23°C | 4,000 | 4,000 | 30,000 | 30,000 | 5,500 | 5,500 | 8,000 | 8,000 |
---|
Mixing ratio | 1:1 | 1:1 | 1:1 | 1:1 |
---|
Pot life *1 | 23°C | 30 s | 2 min | 3 min | 6 min |
---|
Set time *2 | 23°C | 3 min | 4 min | 6 min | 20 min |
---|
Adhesive property | Tensile shear strength | MPa | 23.2 | 19.4 | 26.0 | 21.1 |
---|
T-peel strength | N/mm | 5.0 | 3.6 | 3.7 | 4.2 |
---|
Curing properties | Hardness | Shore D | 68 | 65 | 72 | 66 |
---|
Glass transfer point | °C | 83 | 78 | 90 | 79 |
---|
Elastic modulus | MPa | 767 | 742 | 935 | 778 |
---|
Breaking strength | MPa | 16.2 | 14.0 | 19.0 | 16.1 |
---|
Elongation at break | % | 26 | 8 | 6 | 25 |
---|
Capacity | 600g set | 50g set | 50g set | 600g set |
---|
| 10kg | 600g set | 2kg |
|
|
|
|
|
|
|
|
High heat resistance type
| Y611BLACK S | Y612BLACK |
---|
Agent A | Agent B | Agent A | Agent B |
---|
Application / Properties / Features | Hight strength / High heat resistance |
---|
Base | Acrylic resin | Acrylic resin |
---|
External appearance | Light yellow | Black | Light yellow | Black |
---|
Viscosity | Pa・s/23°C | 3,000 | 3,000 | 15,000 | 15,000 |
---|
Mixing ratio | 1:1 | 1:1 |
---|
Pot life *1 | 23°C | 3 min | 1 min |
---|
Set time *2 | 23°C | 7 min | 3 min |
---|
Adhesive property | Tensile shear strength | MPa | 28.4 | 29.2 |
---|
T-peel strength | N/mm | 4.2 | 4.3 |
---|
Curing properties | Hardness | Shore D | 84 | 86 |
---|
Glass transfer point | °C | 123 | 127 |
---|
Elastic modulus | MPa | 1558 | 1615 |
---|
Breaking strength | MPa | 32.9 | 33.7 |
---|
Elongation at break | % | 3.5 | 3.2 |
---|
Capacity | 600g set | 600g set |
---|
10kg/BIB | 10kg/BIB |
Flexible type
| Y618LD | Y618H | Y630D |
---|
Agent A | Agent B | Agent A | Agent B | Agent A | Agent B |
---|
Application / Properties / Features | Flexible / Low distortion | Hight strength / High heat resistance |
---|
Base | Acrylic resin | Acrylic resin | Acrylic resin |
---|
External appearance | Red | Blue | Light yellow | Light green | Light yellow | Light green |
---|
Viscosity | Pa・s/23°C | 5,000 | 5,000 | 15,000 | 15,000 | 4,000 | 4,000 |
---|
Mixing ratio | 1:1 | 1:1 | 1:1 |
---|
Pot life *1 | 23°C | 2 min | 2 min 30 s | 1 min 30 s |
---|
Set time *2 | 23°C | 7 min | 10 min | 4 min 30 s |
---|
Adhesive property | Tensile shear strength | MPa | 14.2 | 15.7 | 25.3 |
---|
T-peel strength | N/mm | 5.9 | 5 | 4.6 |
---|
Curing properties | Hardness | Shore D | 47 | 55 | 83 |
---|
Glass transfer point | °C | 61 |
| 118 |
---|
Elastic modulus | MPa | 451 |
| 2414 |
---|
Breaking strength | MPa | 10.5 | 10.6 | 32.1 |
---|
Elongation at break | % | 40 | 51 | 2 |
---|
Capacity | 600g set | 190mL set | 600g set |
---|
10kg/BIB |
|
|
|
Conventional type SGA Y650 (*Odorous)
| Y650 |
---|
Agent A | Agent B |
---|
Base | Acrylic resin |
---|
External appearance | Blue | Red |
---|
Viscosity | mPa・s/23°C | 3,220 | 3,320 |
---|
Mixing ratio | 1:1 |
---|
Pot life *1 | 23°C | 2 min 30 s |
---|
Set time *2 | 23°C | 4 min 30 s |
---|
Adhesive property | Tensile shear strength | MPa | 23.8 |
---|
T-peel strength | N/mm | 4.6 |
---|
Curing properties | Hardness | Shore D | 60 |
---|
Glass transfer point | °C | 83 |
---|
Elastic modulus | MPa | 740 |
---|
Breaking strength | MPa | 16.1 |
---|
Elongation at break | % | 25 |
---|
Capacity | 2.5kg
|
---|