Brand: CEMEDINE
Welding Process / Painting Process / Components
Product Name: Automobiles Adhesive
Specifications:
| Welding Process |
---|
Mastic Adhesive | Spot Sealer | Hemming Adhesive | Structural Adhesive |
---|
Application | Hood/Bonne | Wheel House in section | Door | The vehicle body frame |
---|
Features | Solventless type | Solventless type | Solventless type | Solventless type |
---|
Heat Curing | Thermosetting | Dischargeable in Room Temperature | Dischargeable in Room Temperature ONE-PART HEAT CURING TYPE |
Filling Adhesive | Filling Adhesive | One-Component Thermosetting Adhesive for Oil Surface | Oil surface Adhesive |
Dichargeable with Pump in Room Temperature | Pump Dischargeable in Room Temperature |
|
|
Good shower resistance | Good shower resistance |
|
|
Main Composition | Synthetic rubber | Synthetic resin | Epoxy resin | Epoxy resin |
---|
Appearance | High viscosity uniform paste | High viscosity uniform paste | High viscosity uniform paste | High viscosity uniform paste |
---|
Viscosity | 200~400 Pa・s | 200~400 Pa・s | 200~300 Pa・s | 200~300 Pa・s |
---|
Density | g/cm3 | 1.3~1.5 | 1.3~1.5 | 1.3~1.5 | 1.2~1.4 |
---|
Solids content | 95%≤ | 98%≤ | 98%≤ | 98%≤ |
---|
Peel strength | 200~1000 kPa | 100~300 kPa | 15~20 kPa | 15~20 kPa |
---|
Hardness | 10~40 HSA |
|
|
|
---|
Painting Process|Features
Under Body Coating (UBC)
Acryl Sol or PVC Sol- based plastisol coating to automotive underfloor and rustproof chip for wheelhouse.
Spray Application with airless spray is possible.
Various UBS aimed for Soundproof, Thin film weight reduction and High physical property for thin film can be offered.
Coating Type Damping Material
ACRYLIC EMULSION-based Coating Material aimed for vibration reduction of vehicle body.
Application with airless bump is possible.
Baking hardenable type (Recommended baking temp.:120-160°C)
Baking hardening creates forming foamed film and excellent dumping performance.
Sprayable melt sheet
Sound deadening (Reduce sound level)
Vibration reduction
Weight reduction
Easy vertical application
Space save
Improve the paint quality
Body Sealer
PVC Sol - based water stop and rustproof plastisol coating for outside and inside panel of automobile.
Spray application with airless spraying is possible.
In addition to standard type, low VOC type can be offered.
Interlayer Resistance Chip
PVC Sol - based plastisol coating for automotive anti-chipping.
Spray Application with airless spray is possible.
Low viscosity enables excellent spray performance.
By thinly coating on rocker parts (SIDE SILL), excellent membrane property is contributed.
Data
| Painting Process |
---|
Under Body Coating (UBC) | Coating Type Damping Material | Body Sealer | Interlayer Resistance Chip |
---|
Usage | Wheelhouse, Under floor | Floor | Interior, Exterior | Rocker |
---|
Features | Airless Spray | Aqueous coating type damping material | Airless Spray | Airless Spray |
---|
Added Various Functions | Thermosetting-type | Added Various Functions | Added Various Functions |
Main Composition | PVC or Acryl resin | Acrylic emulsion | PVC resin | PVC resin |
---|
Appearance | High viscosity uniform Paste | Gray colored Uniform Paste | High viscosity uniform paste | Low Viscosity Uniform Paste |
---|
Viscosity | 60~120 Pa・s | 80~120 Pa・s | 60~120 Pa・s | 5~20 Pa・s |
---|
Density | g/cm3 | 1.3~1.4 | 1.5~1.6 | 1.4~1.6 | 1.3~1.4 |
---|
Solids content | 95%≤ | 80%≤ | 98%≤ | 90%≤ |
---|
Peel strength | 0.3~2 MPa |
| 0.6~2.0 MPa | 1.0~2.0 MPa |
---|
Hardness | 50~70 |
| 60~80 | 50~70 |
---|
Expansion rate |
| 1.6~1.8 times |
|
|
---|
Components|Features
Interior Parts Adhesive
Good spray-usability with uniform adhesiveness to wide surface.
Adhesive for Automobile Interior Trim which enables spray coating with efficient operation for wide surface.
Satisfy the regulated standard of volatile organic compounds (VOCs) for vehicle compartment.
Good adhesiveness to highly-recyclable PP resin, various types of surface skin for automobile interiors, fabric, PP foam, urethane foam, and various types of skin materials such as leather. (Chloroprene Type)
Good adhesiveness to steel plate, ABS, Vinyl chloride, Vinyl chloride foam. (Urethane Type)
High Spraying Usability with uniform application enables low press pressure operation in low temperature and short-time dry condition.
Good endurance ( wet and heat resistance) enables good performance under severe environment.
Adhesive for Brakes
Solvent type One-Component Thermosetting, Phenol Adhesive with excellent in heat resistance.
Good heat resistance of this product is appropriate for adhering brake linings of automobiles and motorcycles, and clutch facings.
To improve resistance for shock, bending, and detachment, we have mixed adhesive grade of thermosetting resin and synthetic rubber with;
Strong adhesiveness at high temperature excelling in heat aging resistance.
Strong in shock, bending, vibration with durability against repetitive heating and loading, and less deterioration in adhesive force.
Good flowability and quick in drying.
Strong resistance to water, oil, solvent, and medical agents.
Data
| Components |
---|
Interior Parts Adhesive | Adhesive for Brakes |
---|
Usage | Door Trim, Baggage Tray, Instrument Panel, Pillar, Trank Cover etc | Drum brake |
---|
Features | Chloroprene Adhesive / Urethane Adhesive | One-Component Thermosetting High Heat Resistance Adhesive |
---|
Solvent type | Solvent type |
Spray Type | Dischargeable in Room Temperature |
Main Composition | Chloroprene Type | Urethane Type | Phenol resin |
---|
Interior for Vehicles | Interior for Vehicles |
Substrate (Mainly PP) x Skin material | One pot type |
Appearance | Transparent, No-colored, Uniform liquid | Transparent, No-colored, Uniform liquid | Light brown, Black Paste |
---|
Viscosity | 150~250 cps | 150~250 cps | 100~20,000 cps |
---|
Density | g/cm3 | 0.7~0.9 | 0.9~1.0 | 0.9~1.1 |
---|
Solids content | 18~25% | 30~40% | 25~55% |
---|
Peel strength | 20N/25mm | 9N/25mm |
|
---|
Creep performance | 180° creep | 180° creep |
|
---|
Room temperature ·80° 0mm | Room temperature ·80° 0mm |
|
Appropriate forced dying condition |
|
| 180~200°C x 15~30min
|
---|